Truer cutting agent test reports

Share This Post

Share on facebook
Share on linkedin
Share on twitter
Share on email

Different kinds of cutting agent containing 0.4% of FC0205 powder were added on the basis of FC0205 powder to compare their effects on material properties. The forming density of the sample was 7.0 g/m³.
I. Effect on mechanical properties

84fa2f5862
bc0ab7122e
Impact on cutting performance: TD-3 and TD-4 have greatly improved the cutting performance of the material.
Cutting test conditions:
Sample diameter Φ70mm, hole to hole spacing of 3mm, 19 holes drilled per sample.

1c57660c76
7c37c5dac7

Third, the effect on the microstructure: no effect on the metallographic organization, pearlite content normal.

24282982820d11cf0be0
            Contains no cutting aids                                              Contains MnS
cc7236398d62b6e4fa5e
                                   TD-3                                                              TD-4

080b0d1606
                                      TD-5

Subscribe To Our Newsletter

Get updates and learn from the best

More To Explore

News

Introduction of Powder Metallurgy Process

Powder metallurgical materials are materials made directly from several metal powders, or metal powders and non-metal powders, through preparation, pressing and forming, sintering and post-treatment, without melting and casting. Powder metallurgy is a combination of metal metallurgical processes and ceramic sintering processes, it usually has the following processes. Powder Preparation And Compression Moulding The powder

News

Application And Features of Powder Metallurgy Products

Powder metallurgy products usually refer to products made from metal powders (or mixtures of metal and non-metal powders) through a forming and sintering process. Powder metallurgy products are usually used in a wide range of applications, from general machinery manufacturing to precision instruments; from hardware tools to large machinery; from the electronics industry to motor

en_USEnglish
Scroll to Top